1,75 mm Taulman T-glase - Nylon - Green

Like PLA filament, T-glase is printed at lower temperatures. The optimal printing temperature for printing with T-glase filament is about 212°C  to 224°C. However it will print down to 207°C  and up to about 235°C. T-glase prints easily to acrylic, glass, Kapton and other platforms. It has excellent bridging features and has very little to zero warpage, which makes it an excellent material for printing large objects. Also nice to know, T-glase prints without any odors or fumes.

T-glase filament comes on a spool with approximately 450 grams of filament wrapped around it and is available in 1.75mm and 2.85mm diameter.

Features of Taulman T-glase filament

• Taulman T-glase is Manufactured in the U.S.A.;
• Very High Strength;
• Optimum printing temperature is about 212°C to 224°C, but will print down to 207°C and up to about 235°C;
• Taulman T-glase is FDA approved, as T-glase is specifically made of FDA approved polymers for direct food contact/containers.  This includes cups and other liquid storage parts as well as utensils;
• T-glase is recyclable. While T-glase is not biodegradable like PLA, it is however 100% reclaimable in a compatible home filament extruder/maker. If you have a home filament extruder/maker you can actually mix in 12% of the total weight in discarded clear water bottles;
• Taulman T-glase’s clarity supports industry’s requirements for non-destructive evaluation of 3D Printed parts;
• T-glase’s very low shrinkage makes printing large flat surfaces a breeze.  And it easily prints to acrylic, glass, Kapton and other platforms;
• T-glase is very impressive at bridging;
• There are no odors or fumes when 3D Printing with T-glase.

Tips and Tricks for using Taulman T-glase Nylon filament

• Taulman T-glase has a slightly higher viscosity than other printing materials.  As the layer height exceeds 50% of the nozzle dia, printing speed should be adjusted downward ~10% - 20%;
• Retraction: due to a slightly higher viscosity, the retraction distance may need to be lengthened;
• Excessive bubbles in the printed thread are an indication of a higher than required print temperature. Reducing Print temperature below 238C will result in less thread opacity due to recombination with the atmosphere, however this will also reduce bonding in layers exceeding 25% of nozzle diameter;
• Shrinkage is equal to ABS and can be controlled using garolite (LE) as a print table cover/plate;
• Heated beds help just as they do for printing with ABS;
• Note: currently Taulman T-glase measures 1.76mm to 1.83mm dia in a slightly oval shape due to the draw and cooling process. The line cross section is constant, however users should make a slight adjustment to their "Material Diameter" (1.78mm - 1.80mm) settings to accommodate this slight variance.

Product Specifications

Our Taulman T-glase 3D printer filament is wrapped on a plastic spool which contains approximately 0.45Kg of filament. Our Taulman T-glase filaments are packed in a silica sealed bag. Please see below some more details with respect to the weight and dimensions of our Taulman T-glase filaments.